PA66 GF20 (A2000D)

Reinforced with 20% of glass fiber on substrate PA66 is called PA66 GF20, it
improves dimensionally stabilized and impact resistance for injection moulding.
Typical Application of PA66 GF 20 (A2000D)
PA GF20 is applied to various precision gears due to its high rigidity,
dimensional stability, noise reduction, wear resistance, quietness, lubrication
and antistatic.
Processing Detail of PA66 GF20 (A2000D)
Other Details of  PA66 GF20 (A2000D)
Physical Property
Ash (20.0% 1 ISO3451/1)
Conditioned 600°C*2h
Density (1285Kg/m3 1 ISO1183)
Conditioned 23°C
Shrinkage Parallel Flow (0.5-0.9 % 1 ISO294-4)
Shrinkage Vertical Flow (0.8-1.1% I ISO294-4)
Mechanical Properties
Tensile strength (145.0MPa 1 ISO527)
Conditioned 5mm/ min
Tensile Strain at Break (2.5% I ISO527)
Conditioned 5mm/min
Notched Impact Strength (8.5KJ/m2 I ISO179)
Conditioned 1.0J
Flexural Strength (235MPa 1ISO178)
Conditioned 2mm/min
Flexural Modulus (6876 MPa I ISO178)
Conditioned 2mm/ min
Thermal Property
Melting Point (260°C I ISO11357)
Hot Deformation Temperature (245*C I ISO75)
Conditioned 1.8MPa
Flammability Class (HB 1UL94)
Conditioned mm
Injection Molding Conditions
Drying Temperature 130°C
Drying Time 3h
Cylinder Temperature 280-300°C
Nozzle Temperature 280-300*C
Tooling Temperature 80-100*C
* Molding conditions are just for reference, please make an adjustment based
on the actual situation！
Want to know the details of modified polyethylene or buy pa6 6 gf50, contact
us.

Minimum Order: 1000 kilograms