PA6 GF50 (A1011J)

PA 6 GF50 is a fiber reinforced plastic made of nylon 6 resin as a base
material and 50% glass fiber as a reinforcing filler, and various processing
aids be added.
Typical Application of PA6 GF50 (A1011J)
PA GF50 is used to manufacture high-strength and high wear-resistant structural
parts of machinery, vehicles, electronics, sports equipment and other fields.
We know that pa6 50gf composite material takes both strength and toughness into
consideration, which is exactly what the suspension control arm needs.

Processing Detail of PA6 GF50 (A1011J)


Other Details of pa6 6 gf50(A1011J)
Physical Property
Ash                     (15.0% 1 ISO3451/1)
Conditioned 600°C*2h
Density (1250Kg/m3 1 ISO1183)
Conditioned 23°C
Shrinkage Parallel Flow (0.5-0.7 % 1 ISO294-4)
Shrinkage Vertical Flow (0.7-1.1% I ISO294-4)
Mechanical Properties
Tensile strength (125.0MPa 1 ISO527)
Conditioned 5mm/ min
Tensile Strain at Break (2.5% I ISO527)
Conditioned 1.0J
Notched Impact Strength (125 0MPa I ISO527)
Conditioned 2mm/min
Flexural Strength (190MPa 1ISO178)
Conditioned 2mm/min
Flexural Modulus (5700 MPa I ISO178)
Conditioned 5mm/ min
Thermal Property
Melting Point (220°C I ISO11357)
Hot Deformation Temperature (175*C I ISO75)
Conditioned 1.8MPa
Flammability Class (HB 1UL94)
Conditioned mm
Injection Molding Conditions
Drying Temperature 130°C
Drying Time 3h
Cylinder Temperature 240-260°C
Nozzle Temperature 240-260*C
Tooling Temperature 80*C

As one of masterbatch producers, Anmei provides pa6 plastic material, modified
polyolefin, master batches and etc. For more information, please feel free to
contact us!