PA6 GF45 (A1011I)

Polyamide 6 reinforced with 45% Glass Fibers that is PA GF45, medium viscosity
and dimensional stability, this PA6 plastic material has excellent rigidity and
high tensile and compressive strength successfully applying to engineering
structure parts of mechanical engineering and in the automotive industry. 
Typical Application of PA6 GF45 (A1011I)
PA6 GF45 is used in turbines, propellers, screws, nuts, washers and other
components with high rigidity and dimensional stability and heat-resistant
aging, as well as fishing tackle reels, racket frames and other components with
high mechanical strength, good toughness, higher tensile and compressive
strength.

Other Details of PA6 GF45 (A1011I)
Physical Property

Ash                     (15.0% 1 ISO3451/1)
Conditioned 600°C*2h
Density (1250Kg/m3 1 ISO1183)
Conditioned 23°C
Shrinkage Parallel Flow (0.5-0.7 % 1 ISO294-4)
Shrinkage Vertical Flow (0.7-1.1% I ISO294-4)
Mechanical Properties
Tensile strength (125.0MPa 1 ISO527)
Conditioned 5mm/ min
Tensile Strain at Break (2.5% I ISO527)
Conditioned 1.0J
Notched Impact Strength (125 0MPa I ISO527)
Conditioned 2mm/min
Flexural Strength (190MPa 1ISO178)
Conditioned 2mm/min
Flexural Modulus (5700 MPa I ISO178)
Conditioned 5mm/ min
Thermal Property
Melting Point (220°C I ISO11357)
Hot Deformation Temperature (175*C I ISO75)
Conditioned 1.8MPa
Flammability Class (HB 1UL94)
Conditioned mm
Injection Molding Conditions
Drying Temperature 130°C
Drying Time 3h
Cylinder Temperature 240-260°C
Nozzle Temperature 240-260*C
Tooling Temperature 80*C

* Molding conditions are just for reference, please make an adjustment based
on the actual situation！

As one of engineering plastic manufacturers, Anmei provides pa6 plastic
material, modified polyolefin, master batches and etc. For more information,
please feel free to contact us!

Minimum Order: 1000 kilograms

Click to Enlarge