Low Temperature-resistance TPO

The modification of ATP for polyolefin elastomers mainly reflects the following
technical characteristics:

1. Improved Low-temperature Resistance

In the application of cable insulant, the modification TPO of ATP can not only
meet the requirement of electric performance from the insulant but also display
a more broad temperature resistant character——displaying excellent mechanical
properties and aging properties at the test temperature of -50℃—+125℃. So,
this is the optimized insulant for wires and cables which have special
requirements for low-temperature resistance.

2. Improved shrinkage resistance

The jacket made up of TPO wire and cable insulant from ATP keeps its section
surface smooth and orderly with little retraction rate after immersing in
solder machine （350℃/2”）. In the application of high-temperature-resistant
cables (temperature≤125℃) such as charging vehicle cables (EV Cable),
equipment connection cables, etc., the jacket made up of TPO wire and cable
insulant from ATP takes the place of XLPE materials to meet the requirements of
insulant high-temperature aging and shrinkage for nominal cables. And this can
simplify the processing procedures by a large margin and improve the processing
efficiency and yield.

Application: TPO has the characteristics of small specific gravity, good impact
strength, and low-temperature brittleness, and is suitable for applications in
the cable industry.

Technical Data of Low Temperature-resistance TPO
Technical Data Sheet Model
Material Properties Test Standard Test Condition Unit 2895F-
ESS-1008S
General Characteristics Material Category - - -
Appearance(Light/Semi-matte/Frosted) - - -
Extrusion/Injection - - -
Physical Characteristics Hardness ISO 48 15S Shore A 97
Proportion ISO 1183 - g/cm³ 0.93
Melt Index ISO 1133-1:2011 190℃/2.16kg g/10min 1.7
Brittle Temperature ISO 812 - ℃
Mechanical Properties Elongation ISO37:2017 200mm/min %
590
Tensile Strength ISO37:2017 200mm/min Mpa 33.367
Tearing Strength ISO34-1:2015 500mm/min KN/m
Hot Air Aging Elongation Retention Rate ISO37:2017 - %
Tensile Strength Retention Rate ISO37:2017 - %
Electrical Performance Volume Resistivity ASTM D257 - Ohm-cm
Permittivity ASTM D150 - -
Combustion Performance Vertical Burning Test UL 94 3.0/6.0mm -
Oxygen Index ASTM D2863 - %
Feature

As one of the most professional polymer compounding companies, we provide
polymer compound, tpo polyolefin, polymer thermoplastic, tpe elastomero
termoplastico and etc. For more information, please feel free to contact us!

Minimum Order: 500 kilograms

Click to Enlarge