Hot Dipped Iron Wire

Hot dipped galvanized wire is a kind of wire going through hot dipped
galvanizing treatment.

Hot-dipped galvanizing is a physical reaction. After the chlorhydric acid pool
and water pool, the iron wire will go through the drying panel and then enter
the zinc stove. Hot-dip galvanizing is a form of galvanization. It is the
process of coating iron, steel, or aluminum with a thin zinc layer, by passing
the metal through a molten bath of zinc at a temperature of around 860 °F (460
°C). When exposed to the atmosphere, the pure zinc (Zn) reacts with oxygen
(O2) to form zinc oxide (ZnO), which further reacts with carbon dioxide (CO2)
to form zinc carbonate(ZnCO3), a usually dull grey, fairly strong material that
stops further corrosion in many circumstances, protecting the steel below from
the elements.

Customized products

2.54mm hot dipped galvanized wire (for making chain link mesh),the tolerance
for wire diameter is ±0.02mm.The weight of per coil is 500kg and the coil
inner diameter is 40 to 50 cm.
3.65mm hot dipped galvanized wire (Zinc thickness: min. 85.4g/M2,Wire tolerance
±0.02mm,500kg/coil)
wire,hot-dipped galvanized iron, 18 Ga ASTM A-641 for new spray shields



Material : Low carbon steel wire, medium carbon steel wire and high carbon
steel wire.

Tensile Strength: 400--500MPA

Hot dipped iron wire Usage: It mainly used in communication equipment, medical
equipment and weaving nets, brushes, cables, filters, high pressure pipe,
construction, handicrafts and other industries.

Standard wire gauge: 8# - 24#.(See the below table)

Click to Enlarge